Usage Of Cement
 
Portland Cement
Musa Yapi CEM I 52,5 N
Musa Yapi CEM I 52.5 R
Musa Yapi CEM I 42,5  N
Musa Yapi CEM I 42,5 R
Musa Yapi CEM II/A-P 42.5 R
Musa Yapi CEM III A(S) 42,5 N
Musa Yapi CEM II B(S) 52,5
Musa Yapi CEM III/B(S) 42,5N
Musa Yapi CEM IV/B (P) 32.5 R
Musa Yapi CEM V A (PS) 32.5
Musa Yapi OIL WELL CEMENT
Musa Yapi SRC 32,5 R
Musa Yapi SRC 42,5R
Musa Yapi SRC 42,5 CLINKER
Musa Yapi PORLAND CLINKER
Musa Yapi WHİTE CEMENT

 
 
ANALYSIS REPORT
Date:12.06.2009
No:281
 
Musa Yapı
TYPE : COMPOSITE CEMENT CEM V/A P-S 32,5 R
STADARD:TS EN 197-1
TAKEN FROM:PACKING UNIT
DATE:01.06.2009-07.06.2009


  Analysis Results Standard     Standart Analysis Results
CHYMICAL ANALYSIS Total SiO2   30,89 PHYSICAL ANALYSIS Specific Gravity gr cm3   2,89
Insoluble Residue     Water Demand %    
CaO   44,88 Set Time Inıtial Hour min 01.15 03:00
MgO   2,08 Fial Hour    
      MECHANICAL
TESTS
Soundness mm max 10,0  
Fineness Specific Surface cm2 gr  
Residue 45 µ %
           
SO3 max.3,50 2,74      
Na2O     Prizm : 40x40=160mm
Mixture : 1/3
Water Cement : 0,5
K2O    
Total Alkali    
CI‾ max.0,1000 0,0277
Additive Amount    
Loss On Ignition   4,59  
Compessivee Strength
Day Standard Analysis Results
     
1    
2 min.10,0 11,3
7    
f.Cao   0,40 28 32,5 -52,5  

28 Days compressive strength of the sample taken at 27.04.2009-03.05.2009 is 59,3 N/mm2)
This Report cannot be copied without the permission of the test laboratory
Test results bellong to the sample defined above.